Nails Q195 SAE1008 Low Carbon Steel Wire Rods

• Standard: ASTM, JIS, GB, AISI, DIN
• Certification: ISO
• Surface Treatment: Polished
• Technique: Hot Rolled
• Application: Make Nails
• Edge: No
• Model NO.: Q195 SAE1008
• Stock: Stock
• Diameter: 5.5mm 6.5mm 7.0mm 8.0mm 10mm 12mm
• Grade: SAE1006 SAE1008 SAE1010 SAE1012
• Transport Package: Standard Seaworthy Exporting Package
• Specification: SAE1008
• Trademark: FUBANG
• Origin: China
• HS Code: 7227909000

Product Description

Nails Q195 SAE1008 Low Carbon Steel Wire Rods
Product description
Processing Technic: Hot Rolled
Grade: SAE1006  SAE1008 SAE1010 SAE1012  GBQ195 Q235
Coil Weight: about 2 metric tons/coil
Size: 5.5mm,6.5mm,7.0mm,8.0mm,9.0mm,10.mm,11.0mm,12.0mm

Application
a).uesed for construction of reinforced concrete structure for reinforcement
b).used for nail making
c).used for construction as binding wire
d).uesd for tie wire and baling wire
e).used for making for wire mesh

Product No. 1: High Speed Hot rolled low carbon steel wire rods

Grade	Application	Size(mm)	Standard	Delivery Status	Notes
Q195	Mainly used for wire drawing and other general purpose.  Applicable to the construction, drawing wires and other general purpose.	Φ5.5-Φ16.0	GB/T701-2008	Hot Rolled	Wire Rod Unit weight about 2000Kg
Q215		Φ5.5-Φ16.0	GB/T701-2008	Hot Rolled
Q235		Φ5.5-Φ16.0	GB/T701-2008	Hot Rolled
HPB235	For the concrete structure engineering.	Φ6.5-Φ16.0	GB/T1499.1-2008	Hot Rolled

Product No. 2: High Speed Hot rolled Carbon structural steel wire rods

Grade	Application	Size(mm)	Standard	Delivery Status	Notes
1006B 1008B 1012B 1017B 1018B	Mainly used for wire drawing, cold drawn or cold rolled steel wires.	Φ5.5-Φ16.0	ASTM A510M & SAE Grade was used here.	Hot Rolled	Products of the other grades and chemical composition, specified in the contract by the supplier and demander, can be supplied.

Product No. 3: High Speed Hot rolled low alloy steel wire rods

Grade	Application	Size(mm)	Standard	Delivery Status	Notes
HPB300	For the concrete structure engineering.	Φ5.5-Φ16.0	GB/T1499.1-2008	Hot Rolled	Wire Rod Unit weight about 2000Kg. 120t converter, refining furnace, protective casting.
HRB400		Φ5.5-Φ16.0	GB/T1499.2-2008	Hot Rolled
HRB400E		Φ5.5-Φ16.0	GB/T1499.2-2008	Hot Rolled
30MnSi	For the application of port concrete pipe pile, high buildings concrete pipe pile foundation, and the concrete  pier pipe pile.	Φ5.5-Φ16.0	GB/T24587-2009	Hot Rolled

Chemical Composition & Mechanical Properties

chemical Composition							Mechanical Properties
Grade	C	Mn	Si(≤)	P(≤)	S(≤)	B	Y.S.(Mpa)	T.S.(Mpa)	Elongation(%)
Q195	0.06-0.12	0.25-0.50	0.3	0.05	0.05	0.0008	≥195	315-430	33
Q235	0.12-0.20	0.30-0.70	0.3	0.05	0.05	0.0008	≥235	375-500	26
SAE1006	≤0.08	0.25-0.40	0.3	0.05	0.04	0.0008	≥210	210-370	32
SAE1008	≤0.10	0.30-0.50	0.3	0.05	0.04	0.0008	≥195	315-430	30