HIPS Granule / HIPS Raw Material / Virgin or Recycled HIPS Granule

• Customization: Available
• Material: High Impact Polystyrene/HIPS
• Usage: General Plastics
• Model NO.: 400060
• Plastic Properties After Heated: Thermosetting Plastic
• Color: White
• Transport Package: 25kgs/Bag
• Specification: Virgin HIPS Granules
• Trademark: Virgin HIPS Granules
• Origin: China
• HS Code: 3903199000
• Production Capacity: 500mt/Month

Product Description

High Impact Polystyrene HIPS

 

1/ Product property

    High impact polystyrene, or HIPS, is a versatile plastic resin used in the manufacture of numerous products. Easy to fabricate, this resilient material costs little to produce and offers applications in many industries. Its physical properties permit flexible machining and surface applications such as paints and adhesives.

2/ Specification

Performance of Projects		Test condition	Testing Method	Test Data	Data Unit
Others	Bending modulus	---	ASTM D-790	2.3(2260)	kg/cm2×104(MPa)
Basic  Properties	Melt Flow Index	---	ASTM D-1238	5.5	g/10min
Mechanical  Properties	IZOD impact strength	---	ASTM D-256	11.0(108)	kg-cm/cm(J/m)
	Tensile strength	---	ASTM D-638	220(22)	kg/cm2(MPa)
	Tensile modulus	---	ASTM D-638	1.5(1470)	kg/cm2×104(MPa)
	elongation	---	ASTM D-638	40	%
	Bending strength	---	ASTM D-790	440(43)	kg/cm2(MPa)
Thermal  Properties	Vicat Softening  point	---	ASTM D-1525	95	°C
	Heat distortin temperature	---	ASTM D-1525	88	°C
Other	Residucl monomer	---	---	700	ppm max
	Burning rate	1/16"	UL 94	NC	HB

 

Raw materials description
Standard	Injection molding grade		Colour		White
Application	High impact, high heat-resisting, low temperature resistance,good regidity,according with food hygienic standard, be widely used in toy and home appliances manufacture.
Remark	High impact, high heat-resisting, extrusion molding.
Raw materials technique data
Property items		Test condition		Method		Test result	Units
Basic performance	Melt flow rate	200°C/5kg		ISO 1133		4.6	g/10min
	Density			ISO 1183		1.04	g/cm^3
	Water absorption			ISO 62		<0.1	%
Physical property	Process contractibility rate			ISO 294		0.4-0.7	%
Mechanical behavior	Stretch yield stress	23°C		ISO 527		23	Mpa
	Percentage elongation	23°C		ISO 527		45	%
	flexural strengh	23°C		ISO 178		46	Mpa
	Flexural modulus	23°C		ISO 178		2260	Mpa
	Izod impact	23°C		ISO 180		115	j/m
	Rockwell hardness	23°C		ASTMD-785		65	L
Thermal property	Vicat softening point	B10/oil		ISO 306		95	°C
	distortion temperature(non-anneal)	1.82Mpa		ISO 75-2		79	°C
Other propery	Fire resistance			UL 94		HB
	residual monomer					<400	ppm max

3/ Application

PS peripheral appliances, electrical appliances, stationery .
The material can be used as packaging filler, pressed into board, molded into products, or delivered on sheets or rolls. Its characteristic dimensional stability permits it to be employed in low strength construction, and in its natural translucent form makes it suitable for food processing applications.