Plastic Raw Material PA Polyamide-6

• Customization: Available
• Usage: General Plastics, General Plastics, Engineering Plastics
• Plastic Properties After Heated: Thermoplastic Plastics, Thermoplastic Plastics
• Model NO.: polyamide-6
• Plastic Forming Method: Extrusion, Extrusion
• Color: White, White
• Environmental Protection: Yes
• Appearance: Granulars
• Kind: Plastic Raw Materials
• Material: Polyamide(Nylon 6.66)/PA
• Transport Package: 25kg, 20mt/Container
• Origin: China
• Production Capacity: 5000ton

Product Description

1. Product Description
Modified PA6 is a high quality thermoplastic engineering plastic in the form of granulate for injection moulding and extrusion made by virgin PA6 materials.

Key feature:

30%GF
High mechanical strength;
Heat stabilized
    
Application:

Engine parts
like intake manifold etc.

Data sheet is as below:
 

Property	Unit	Test standard	Test condition	GF reinforced PA6
				BG6TBK-S02
Physical property
Density	g/cm^3	ISO1183		1.36
Filler content	%	ISO 1172		GF30
Mold shrinkage	%	ISO 294	Parallel	0.2
			Vertical	0.6
Mechanical property
Tensile strength	MPa	ISO 527	I type sample              50mm/min	180
Elongation at break	%	ISO 527	I type sample      50mm/min           gauge length 50mm	3
Flexural strength	MPa	ISO 178	23ºC10mm/min	240
Flexural modulus	MPa	ISO 178	23ºC10mm/min	8500
Izod impact strength (notched)	KJ/m^2	ISO 180	23ºC	16
Charpy impact strength (unnotched)	KJ/m^2	ISO179	23ºC	95
Thermal property
Melting point	ºC	ISO11357-1		220
HDT	ºC	ISO 75	0.45Mpa	219
		ISO 75	1.8Mpa	205
Flammability
Flammability	Class	UL-94		HB
GWIT		IEC 60695-2-13		-
Electrical property
Surface resistivity	Ω	IEC60093		1.00E+14
Volume resistivity	Ω·cm	IEC60093		1.00E+15

2. Applications 
Civilian and industrial high-spinning, conventional spinning, food-grade and medical-grade packing film, carpet yarn, fishing nets, ribbon, trimmer line, direct injection molding of engineering plastics, mechanical parts, high-loaded mechanical components, electric switchplugins, equipment, modification of composite materials, etc.