White/Black MDPE for Cable Shelth

• CAS No.: 9002-88-4
• Material: Polyethylene/PE
• Usage: General Plastics
• Plastic Properties After Heated: Thermosetting Plastic
• Plastic Forming Method: Injection
• Color: White
• Transport Package: 25kg/Bag, 20ton/Container
• Trademark: sinopec
• Origin: China
• Production Capacity: 5000ton

Product Description

White/Black MDPE for Cable Shelth
Product Description
Model NO.:MDPE
Material:Low Density Polyethylene/LDPE
Usage:General Plastics, Engineering Plastics, Specialty Plastics
Plastic Properties After Heated:Thermoplastic Plastics
Plastic Forming Method:Film Pressure
Color:Black
Product Name:MDPE Resin Black
Grade:Blow Molding/Injection Molding Film/Extrusion Gra
Mass Density:0.941-0.959 g/cm3
Melt Flow Rate(190 Centidegree /2.16kg):<=1.0g/Min
Tensile Yield Strength:≥19.0MPa
Flexural Modulus:≥965MPa
Elongation@ Break:≥400
Price Term:EXW FOB CIF
Certificate:SGS
Company Nature:Trading Company & Factory Price
Export Markets:Global

Additional Info.

Packing:25kg/Bag
Standard:SGS certificated
Origin: China
HS Code:390110001
Production Capacity:200mt/Week for PE Granules

Product Description

Product Name:black MDPE for cable shelth/pipe adaptor

offer high quality HDPE Granules that is a multi-purpose polyethylene used in diverse industrial sectors for specific applications. These HDPE Granules are sourced from reliable manufacturers and is highly appreciated by clients for superior quality. We provide the HDPE Granules at nominal rates to clients.

Technical Data of black MDPE for cable shelth/pipe adaptor

Physical Properties	Metric	English	Comments
Density	0.930 - 1.05 g/cc	0.0336 - 0.0379 lb/in³	Average value: 0.945 g/cc Grade Count:22
Environmental Stress Crack Resistance	1000 - 5000 hour	1000 - 5000 hour	Average value: 2290 hour Grade Count:10
	>= 2000 hour @Temperature 80.0 - 80.0 °C	>= 2000 hour @Temperature 176 - 176 °F	Average value: 2000 hour Grade Count:2
Melt Flow	0.200 - 21.0 g/10 min	0.200 - 21.0 g/10 min	Average value: 3.84 g/10 min Grade Count:22
Mechanical Properties	Metric	English	Comments
Hardness, Shore D	48.0 - 69.0	48.0 - 69.0	Average value: 57.2 Grade Count:11
Tensile Strength, Ultimate	12.5 - 33.1 MPa	1810 - 4800 psi	Average value: 22.8 MPa Grade Count:5
Tensile Strength, Yield	13.8 - 31.0 MPa	2000 - 4500 psi	Average value: 19.7 MPa Grade Count:16
Elongation at Break	50.0 - 1000 %	50.0 - 1000 %	Average value: 510 % Grade Count:17
Modulus of Elasticity	0.800 GPa	116 ksi	Average value: 0.800 GPa Grade Count:3
Flexural Modulus	0.590 - 0.840 GPa	85.6 - 122 ksi	Average value: 0.694 GPa Grade Count:9
Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+15 - 3.00e+16 ohm-cm	1.00e+15 - 3.00e+16 ohm-cm	Average value: 1.16e+16 ohm-cm Grade Count:7
Dielectric Constant	2.30 - 2.55	2.30 - 2.55	Average value: 2.38 Grade Count:3
Dielectric Strength	21.7 - 39.4 kV/mm	550 - 1000 kV/in	Average value: 29.2 kV/mm Grade Count:6
Dissipation Factor	0.000500	0.000500	Average value: 0.000500 Grade Count:3
Thermal Properties	Metric	English	Comments
Melting Point	126 - 128 °C	259 - 262 °F	Average value: 126 °C Grade Count:5
Vicat Softening Point	114 - 127 °C	237 - 261 °F	Average value: 119 °C Grade Count:4
Brittleness Temperature	-100 - -70.0 °C	-148 - -94.0 °F	Average value: -79.3 °C Grade Count:8
Processing Properties	Metric	English	Comments
Processing Temperature	180 - 240 °C	356 - 464 °F	Average value: 210 °C Grade Count:6
Die Temperature	185 - 218 °C	365 - 425 °F	Average value: 198 °C Grade Count:7
Melt Temperature	160 - 230 °C	320 - 446 °F	Average value: 190 °C Grade Count:8
Head Temperature	185 - 210 °C	365 - 410 °F	Average value: 196 °C Grade Count:6