High density polyethylene PE 100
SPECIFICATION
|
Physical |
Nominal Value |
Unit |
Test Method |
|
Density |
0.959 |
g/cm³ |
ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) |
0.23 |
g/10 min |
ISO 1133 |
|
Carbon Black Content |
2.3 |
% |
ISO 6964 |
|
Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus (23°C, 2.00 mm, Compression Molded) |
900 |
MPa |
ISO 527-2/1BA/50 |
|
Tensile Stress (Yield, 23°C, 2.00 mm, Compression Molded) |
23.0 |
MPa |
ISO 527-2/1BA/50 |
|
Tensile Strain (Yield, 23°C, 2.00 mm, Compression Molded) |
9.0 |
% |
ISO 527-2/1BA/50 |
|
Impact |
Nominal Value |
Unit |
Test Method |
|
Charpy Notched Impact Strength |
|
|
ISO 179/1eA |
|
-30°C |
13 |
kJ/m² |
|
|
23°C |
26 |
kJ/m² |
|
|
Hardness |
Nominal Value |
Unit |
Test Method |
|
Shore Hardness (Shore D, Compression Molded) |
63 |
|
ISO 868 |
|
Thermal |
Nominal Value |
Unit |
Test Method |
|
Vicat Softening Temperature |
74.0 |
°C |
ISO 306/B |
|
Melting Temperature (DSC) |
124 to 128 |
°C |
DIN 53765 |
|
Oxidation Induction Time (210°C) |
> 20 |
min |
EN 728 |