| Material: | Low Density Polyethylene/LDPE |
|---|---|
| Usage: | General Plastics |
| Plastic Properties After Heated: | Thermosetting Plastic |
| Color: | White |
| Transport Package: | 25kg/Bag |
| Specification: | Recycled LDPE |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 15 | g/10min |
| Density | 0.922 | g/cm3 |
| Tensile Yield Strength | 7 | Mpa |
| Elongation at Break | 75 | % |
| Wien Softening Point | 85 | °C |
| Packing | In 25 kg PP woven bags,20MT/20'FCL | |
LDPE film grade
| Tests | Value | Unit |
| Melt Flow Rate (MFR) | 2 | g/10min |
| Density | 0.9225 | g/cm3 |
| Tensile Strength | 9 | Mpa |
| Elongation at Break | 500 | % |
| Fish eye max(0.3-2mm) | 30 | n/1200cm2 |
| Stripes | 20 | cm/20m3 |
| Packing | In 25 kg PP woven bags,20MT/20'FCL | |
| ITEM | RESULT | TEST METHOD |
| melt flow rate ( g/10min ) | 2.3 | ASTM D-1238 |
| Density g/cm3 | 0.9 24 | ASTM D-792 |
| Hardness Shore D | 57 | ASTM D-2240 |
| Elongation % | 7 | ASTM D-638 |
| environmental stress crack resistance | 3 | ASTM D-1693 |
| 2% Secant bending modulus psi(MPa) | 167,000(1151) | ASTM D-790 B |
| tensile yield strength ft@lb/in2(kJ/m2) | 20(42) | ASTM D-1822,Type S |
| tensile breaking strength psi(MPa) | 2000(14) | ASTM D-1822,Type S |
| elongation at break % | 250 | ASTM D-638 |