Virgin Granules LLDPE 218W

• Customization: Available
• Material: Linear Low Density Polyethylene/LLDPE
• Usage: General Plastics
• Model NO.: 400060
• Plastic Properties After Heated: Thermosetting Plastic
• Color: White
• Transport Package: 25kg/Bag
• Specification: LLDPE 218W
• Trademark: LLDPE 218W
• Origin: China
• HS Code: 39012000
• Production Capacity: 500mt/Month

Product Description

Specification:

Test item	Unit	Index
Tensile strength	MPa	>=13.5
Rupture elongation	%	>=350
Impact brittle temperature		-76
Impact brittle performance	Failure rate	<=15/30
Heating aging temperature		135+-2
Duration	H	168
Tensile strength change rate	%	+-20
Rupture elongation change rate	%	+-20
Hot drawing	%	<=80
Keep permanent deformation after cooling	%	<=5
Gel contents	%	>=80
Dielectric loss factor		<=1X10-3
Relative dielectric constant		<=2.35
Volume resistivity	O.m	>=1X1014
Dielectric strength	MV/m	>=25

ITEM	UNIT	VALUE
Density	g/cm3	0.945-0.978
MFR (1900C X 2.16KG)	g/10min	≤0.4
Tensile Strength at Yield	Mpa	≥16.0
Tensile Strength	Mpa	≥20
Elongation at Break	%	≥600
Vicat Softening Point	0C	≥110
ESCR	h	≥500
EHCR	h	≥96
Low Temperature                  Impact Strength	0C	-76
Low Temperature            Elongation at Break	%	≥175
Carbon Black Dispersion		≥6
20 0C Volume Resistivity	Ω·m	≥ 1.0 x 1014
Dielectric Strength	MV/m	≥ 35

No.	Property	Unit	Test	Data
1	Melt Flow Index	g/10min	GB/T3682-2000	≤1.0
2	Density	g/cm3	GB/T1033.1-2008	≤0.945
3	Tensile strength	Mpa	GB/T1040.3-2006	≥14.0
4	Elongation at break	%	GB/T1040.3-2006	≥600
5	Brittle temperature at low temperature	ºC	GB/T5470-2008	≤-76
6	ESCR ,FO	H	GB/T2951.41-2008	≥500
7	Tensile strength after thermal aging	Mpa	GB/T2951.12-2008	≥13
8	Elongation after thermal aging	%	GB/T2951.12-2008	≥500
9	Dielectric strength	Mv/m	GB/T1408.1-2006	≥25
10	Volume resistivity	Ω.m	GB/T1410-2006	≥1*1014
11	Change rate of tensile strength after weather aging environment of 0--1008h	%	GB/T12527-2008	±25
	Change rate of elongation after weather aging  environment of 0--1008h	%	GB/T12527-2008	±25
	Change rate of tensile strength after weather aging  environment of 504--1008h	%	GB/T12527-2008	±15
	Change rate of elongation after weather aging environment of 504--1008h	%	GB/T12527-2008

Application:

Grade	Type	MFR (g/10min)	Density (g/cm3)	Application
LD100-AC	Film material	2	0.9225	For agricultural film,shrinkable film,transparent film,laminating film, shopping bag,refrigeration film, medical package,COEX multilayer film, all kinds of packaging bag,LLDPE blending materials
LD100	Film material,  injection molding	2	0.9225	Injection molding, cast film
LD103	Film material	1.05	0.921	For agricultural film,shrinkable film,lining,disposable bag,shopping bag,refrigeration film,COEX multilayer film,all kinds of packaging  bag, LLDPE blendi
LD113	Film material	2.3	0.9205	For agricultural film,shrinkable film,lining,disposable bags, COEX  multilayer,all kinds of packing bags, LLDPE blending materials,  injection molding, power cable insulation peroxide cross-linking, coaxial cable~
LD150	Film material	0.75	0.9225	For agricultural film,shrinkable film,heavyduty packaging film,laminate  film,shopping bag,refrigeration film,COEX multilayer film, all kinds of  packing bags,LLDPE mixed materials,power cable insulation silicane cross-linking, blow molding, tubes and pipes
LD160	Film material	4	0.9225	For lining,transparent film,laminate film,ultrathin film,all kinds of packa ging bag,casting film,injection molding
LD165	Heavy-duty packing  film	0.33	0.922	For large greenhouse film,agricultural film,shrinkable film,lining,power cable insulation silicane cross-linking,communication cable coat,blow molding,tubes and pipes
LD166	Heavy-duty packing  film	0.2	0.9225	For large greenhouse film,shrinkable film,heavy-duty packaging film, power cable insulation silicane cross-linking
SD330	Film material  LLDPE blending  material	2	0.922	For agricultural film,shrinkable film, lining,disposable bag,transparent  film,laminate film,shopping bag,ultrathin film,refrigeration film, medical package,COEX multilayer film,all kinds of packaging bags,general  purpose film,LLDPE blending materials
LD605	Injection molding	6	0.922	Ultrathin film, injection molding
LD615	Injection molding,  master batch	15	0.922	For plastic injection, master batch